We are the resin manufacturer you need!
Structures:Orthophthalic
Processes:Casting Resin
Application:It is soluble in crosslinking monomers such as styrene and has moderate viscosity and high reactivity.
ZC-5397AR resin is an unsaturated polyester resin with phthalic anhydride, maleic anhydride, and standard diols as the main raw materials. It is soluble in crosslinking monomers such as styrene and has moderate viscosity and high reactivity.
ZC-5397AR resin has good toughness, fast curing, and is economical. Suitable for solid surface materials of calcium powder board
| Property | Value | Unit | TM |
| Appearance | Yellow transparent viscous liquid | – | – |
| Acid Value | ≤90 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.35-0.65 | Pa.s | GB/T 7193-2008 |
| Solid Content | 67-72 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time,25℃ | 4.5-9.5 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Casting body has no defects | – | – |
| Barcol Hardness | 30 | – | GB/T 3854-2005 |
| HDT | 55 | ℃ | GB/T 1634-2004 |
| Break Elongation | 6 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 45 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 2200 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 80 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 240 | Mpa | GB/T 2567-2008 |
1. ZC-5397AR resin contains wax, no accelerators, and no thixotropic additives.
2. ZC-5397AR resin is suitable for calcium powder board.
3. Cutting and polishing during the production process should be carried out after sufficient curing.
4. After curing at 60-70 ° C for no less than 3 hours, the product performance is better.
5. Moisture absorption of fillers should be avoided, as excessive moisture content can affect the curing of the product and lead to a decrease in performance.
Net weight is 220 kg, metal barrel.Please contact us for special packaging requirements.