We are the resin manufacturer you need!
Structures:DCPD
Processes:Hand lay-up
Application: Suitable for ordinary fiberglass products, as well as repairing and strengthening stone materials.
ZC-5802PT orthophthalic unsaturated polyester resin derived from the chemical reaction of phthalic anhydride, maleic anhydride and standard diol.
ZC-5802PT resin has low viscosity ，Medium reactivity，Proper strngth and rigidity，Fast post cuere，With wax， Promoted ，Thixotropic ，Wax free，Low shrinkage，Low heat release，Excellent water proof，Good mechanical property，Easy for operation，Good impregnation with fiberglass Suitable for hand lamination and spray up process FRP products with high requirement for stable size like, automobile parts, all kinds of inland river FRP boats and FRP sea boat structural layer. ZC-5802PT has passed CCS certificate , could be used for boat manufacture.
| Property | Value | Unit | TM |
| Appearance | Red turbid viscous liquid | – | – |
| Acid Value | 25-35 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.20-0.50 | Pa.s | GB/T 7193-2008 |
| Solid Content | 54-60 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gelation time,25℃ | 9-60 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | No defects in the casting body | – | – |
| Babbitt Hardness | 40 | – | GB/T 3854-2005 |
| HDT | 65 | ℃ | GB/T 1634-2004 |
| Breake elongation | 2 | % | GB/T 2567-2008 |
| Tensile Strength | 60 | Mpa | GB/T 2567-2008 |
| Tensile modulus | 3700 | Mpa | GB/T 2567-2008 |
| Flexural strength | 100 | Mpa | GB/T 2567-2008 |
| Flexural modulus | 3700 | Mpa | GB/T 2567-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 64 | – | GB/T 3584-2005 |
| Flexural strength | 300 | Mpa | GB/T 1449-2005 |
| Flexural modulus | 16500 | Mpa | GB/T 1449-2005 |
| Tensile strength | 320 | Mpa | GB/T 1447-2005 |
| Tensile modulus | 15500 | Mpa | GB/T 1447-2005 |
ZC-5802PT resin contains thixotropic additives and accelerators, no wax Thixotropic agent will gradually precipitate during storage of thixotropic resin It is a normal phenomenon and should be fully stirred before use.
Net weight 220 kilograms, in metal drums. Special packaging requirements, please contact us.