Structures:Isophthalic Resin
Processes:Hand lay-up,Filament Winding
Application:It has been dissolved in styrene cross-linking monomer and has low viscosity and high reactivity.
ZC-519 resin is based on phthalic anhydride, maleic anhydride and standard diols as the main raw materials Polyunsaturated polyester resin with low viscosity and medium reactivity.
ZC-519 resin has low temperature peak and good mechanical properties for ABS composite acrylic sheet Good adhesion, easy to infiltrate glass fiber, operation is not easy to flow glue. Suitable for injection Process and hand paste process, used for ABS composite acrylic sheet bonding and strengthening.
| Property | Value | Unit | TM |
| Appearance | Red turbidity Viscous liquid | – | – |
| Acid Value | 28-34 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.15-0.3 | Pa.s | GB/T 7193-2008 |
| Solid Content | 59-65 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gelation time 25℃ | 29-35 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | The casting body is free from defects | – | – |
| Barcol hardness | 45 | – | GB/T 3854-2005 |
| HDT | 65 | ℃ | GB/T 1634-2004 |
| Break Elongation | – | Mpa | GB/T 2567-2008 |
| Tensile Strength | 60 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3600 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 100 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3700 | Mpa | GB/T 2567-2008 |
ZC-519 resin contains thixotropic auxiliaries and accelerators, and does not contain wax. thixotropic resin storage process thixotropic agent will gradually precipitate, is a normal phenomenon, should be fully stirred before use.due to the composition of ABS composite acrylic sheet is different Adhesion tests should be carried out before use to ensure its suitability.
Net weight is 220 kg, metal barrel.Please contact us.