We are the resin manufacturer you need!
Structures:DCPD
Processes:Hand lay-up
Application: Suitable for ordinary fiberglass products, as well as repairing and strengthening stone materials.
ZC-DC196 resin DCPD type unsaturated polyester resin manufactured from raw materials like dicyclopentadiene, maleic anhydride, and standard diols .The unsaturated polyester resin has been dissolved in the cross -linking monomer of the styrene, with medium viscosity and medium reaction activity.
ZC-DC196 resin features high -solid and low viscosity, and has good infiltration with glass fiber. FRP has excellent mechanical performance.High strength, good water resistance and heat resistance, wide application range. Suitable for ordinary glass fiber reinforcement products can also be used for the repair and enhancement of stone.
| Property | Value | Unit | TM |
| Appearance | Light yellow transparent viscous liquid | – | – |
| Acid Value | 17-23 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.25-0.45 | Pa.s | GB/T 7193-2008 |
| Solid Content | 68-75 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 5-18 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Casting body no fault | – | – |
| Barcol hardness | 40 | – | GB/T 3854-2005 |
| HDT | 85 | ℃ | GB/T 1634-2004 |
| Break Elongation | 2 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 50 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3200 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 90 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3800 | Mpa | GB/T 2567-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 66 | – | GB/T 3584-2005 |
| Flexural Strength | 330 | Mpa | GB/T 1449-2005 |
| Flexural Modulus | 17000 | Mpa | GB/T 1449-2005 |
| Tensile Strength | 330 | Mpa | GB/T 1447-2005 |
| Tensile Modulus | 17000 | Mpa | GB/T 1447-2005 |
1. ZC-DC196 resin contains wax, excluding promotional agents and thixotropic additives. 2. ZC-DC196 resin is sensitive to light, and it is easy to gel under sunlight, so it should be avoided sunlight before use. Free to open the packaging or expose it to a strong light. 3. Recommendation of the curing system: 0.4-2.0% cobalt (not recommended to contain colorless promoters with copper salt and potassium), and MEKP curing agent is 1.0-2.5%.
4. ZC-DC196 resin FRP performance has the characteristics of high hardness, high heat resistance and other characteristics.
ZC-DC196 resin packaging: net weight 220 kg, metal barrel. Special packaging requirements, please contact us.