We are the resin manufacturer you need!
Structures:Orthophthalic
Processes:Hand lay-up
Application:It is suitable for ordinary fiberglass products.
ZC-196resin is an unsaturated polyester resin with phthalic anhydride, maleic anhydride and standard glycol as the main raw materials. It has been dissolved in cross-linking monomers such as styrene and has high viscosity and medium reactivity.
ZC-196 resin has good strength and rigidity, fast post-curing, and good overall performance. It is suitable for ordinary fiberglass products.
| Property | Value | Unit | TM |
| Appearance | Light yellow transparent viscous liquid | – | – |
| Acid Value | 20-26 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.7-0.8 | Pa.s | GB/T 7193-2008 |
| Solid Content | 62-68 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time | 6-18 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Qualified | – | – |
| Barcol hardness | 42 | – | GB/T 3854-2005 |
| HDT | 60 | ℃ | GB/T 1634-2004 |
| Break Elongation | 2.5 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 60 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3800 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 120 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3800 | Mpa | GB/T 2567-2008 |
| Property | Value | Unit | TM |
| Barcol Hardness | 64 | – | GB/T 3584-2005 |
| Flexural Strength | 300 | Mpa | GB/T 1449-2005 |
| Flexural Modulus | 17000 | Mpa | GB/T 1449-2005 |
| Tensile Strength | 320 | Mpa | GB/T 1447-2005 |
| Tensile Modulus | 16000 | Mpa | GB/T 1447-2005 |
1. ZC-196 resin contains wax and does not contain accelerators and thixotropic additives.
2.If you have higher performance requirements, it is recommended to choose ZC-196TP resin.
Net weight is 220 kg, metal barrel.