We are the resin manufacturer you need!
Structures:Orthophthalic Resin
Processes:Casting Resin
Application:It has been dissolved in crosslinking monomers such as styrene and has moderate viscosity and low reactivity.
ZC-3558PAB resin is a pre promoted unsaturated polyester resin with phthalic anhydride, maleic anhydride, and standard diols as the main raw materials. It has been dissolved in crosslinking monomers such as styrene and has moderate viscosity and low reactivity.
ZC-3558PAB has a light color, high transparency, small shrinkage, and stable curing. Pure resin products have a clear and transparent appearance, light color, and excellent resistance to yellowing. They are suitable for making handicrafts such as imitation crystal, imitation colored glass, and imitation glass frosted.
| Property | Value | Unit | TM |
| Appearance | Yellow transparent viscous liquid | – | – |
| Acid Value | 15-25 | mgKOH/g | GB/T 2895-2008 |
| Viscosity，25℃ | 0.5-0.65 | Pa.s | GB/T 7193-2008 |
| Solid Content | 63-68 | % | GB/T 7193-2008 |
| Thermal Stability,80℃ | ≥24 | h | GB/T 7193-2008 |
| Gel time,25℃ | 3-6 | min | GB/T 7193-2008 |
| Property | Value | Unit | TM |
| Appearance | Casting body has no defects | – | – |
| Barcol Hardness | 40 | – | GB/T 3854-2005 |
| HDT | 47 | ℃ | GB/T 1634-2004 |
| Break Elongation | 4 | Mpa | GB/T 2567-2008 |
| Tensile Strength | 50 | Mpa | GB/T 2567-2008 |
| Tensile Modulus | 3000 | Mpa | GB/T 2567-2008 |
| Flexural Strength | 90 | Mpa | GB/T 2567-2008 |
| Flexural Modulus | 3000 | Mpa | GB/T 2567-2008 |
1. ZC-3558PAB resin contains accelerators, wax and thixotropic additives.
2. Recommended curing system: curing agent M-50 (Akzo Nobel), 0.5~0.8%.
3. Suitable operating environment (temperature 20-30 ° C, humidity<70%) makes production easier to control and improves product performance.
Net weight is 220 kg, metal barrel.Please contact us for special packaging requirements.